Product description
Chester Metal Ceramic T is a two-component epoxy- thixotropic composite resistant to cavitation and abrasive wear.
Examples of recommended applications:
- resurface of worn impellers and pump casings
- repair of marine screws
- resurface of valves and gate valves
- restoration of worn elements exposed to erosion and cavitation
- repair of heat exchanger bottoms
- fan repair
- repair of Kort nozzles
- regeneration of bow thrusters
- flange regeneration.
For complete technical information see the Technical Data Sheet (TDS).
Technical data
| Appearance | paste |
| Mixing ratio: (Base : Reactor) by weight / by volume | 2,9:1 / 2:1 |
| Working life (at 20°C) | 35 min |
| Time to machining (at 20°C) | 5 hours |
| Full chemical resistance (at 20°C) | after 7 days |
| Maximum working temperature | 150°C |
| Heat deflection temperature (HDT) (ISO 75-1) | 85°C |
| Compressive strength (ISO 604) | 120 MPa |
| Flexural strength (ISO 178) | 90 MPa |
| Shear strength for steel (ISO 4587) | 19,6 MPa |
| Pull off adhesion (grit blasted steel) (ISO 4624) | min. 22,0 MPa |
| Impact strength (ISO 179/1fU) | 5,2 kJ/m² |
| Density | 1,99±0,05 g/cm³ |
| Package size | 1 kg, 2 kg, 5 kg |
Documents
Other products
Chester Metal Super
Chester Metal Super SL
Chester Metal Super FE
Chester Metal Special
Chester Metal Ceramic F
Chester Metal Ceramic FSL
Chester Metal Ceramic FHT
Chester Metal Super AL
Chester Metal Super BR
Chester Metal Super MS
Chester Metal Rapid E
Chester Metal Slide
Chester Metal Slide F